History of Fishing Line and Fluorocarbon Fishing Line
January 22, 2021
Angling dates backs thousands of years, with archeologists discovering ancient Egyptian art depicting fisherman using rod, line and hook that is dated from the year 2000 B.C. The time period from 1603 to 1868 saw the development of natural lines out of several different natural products. The first natural line was first made from sericterium(silk glands). The silk gland fibers were spun into line to create the first natural fishing lines. This natural line had ideal characteristics of moderate stiffness and good relative transparency. The greatest limitations were the amount of time required to make the line and the maximum length that could be produced was just over 8 feet. The development and production of natural line in this manner was very innovative and at the time. Line made this way during this period was more expensive than gold for the same weight.
Moths would create silkworm nests and line makers would collect those nests to separate out individual silk gland fibers. These individual silk glands are called sericterium.
The sericterium(silk glands) were removed from the nests and soaked in acetic acid for 1-10 minutes. If they were soaked for too long time of a time, they would become too hard and fragile, breaking easily.
After soaking in acid the sericterium were taken out and stretched to create line.
In 1884 “artifical” line is invented in France by a process that used twisted silk that was mixed with resin and chemicals. This represented the first line that was not made from all natural fibers.
In 1937, Warren Carrosas of DuPont succeeded in synthesizing the world’s first nylon (66 nylon) line. This new synthetic line was a fiber made of water, air and coal, with very high strength and thin as spider silk. Many anglers today commonly refer to nylon lines as monofilament. Technically, any line made with one fiber is a mono or single filament, but many anglers refer to all nylon lines as monofilament.
In 1939, Toyo Rayon (now Toray) succeeded in synthesizing nylon 66 in Japan. In the same year, the company succeeded in producing nylon 66 filament by dry spinning. However, the synthesis required concentrated nitric acid and the equipment could not withstand the acid during production. In 1942, Toray named all synthetic lines polyamides, including nylon 6, “Amiran”. In 1943, Toray received a National Order “Research on the synthesis of raw materials for polyamide-based synthetic fibers and spinning from polymers”, but they discontinued production of synthetic line due to intensifying conditions from World War II in 1944. The launch of the first polyester braided line for hand fishing took place in 1953 from company YGK. YGK continued the innovation of braided lines with the launch of braided polyester line for reels in 1970.
The first fluorocarbon fishing line was a carbon compound “vinylidene fluoride resin” fluorocarbon. Kureha started production in 1970, and in 1971, Japan’s first fluorocarbon leader “Seaguar” debuted. Manufactured using fluorine atoms contained in fluorite. The raw material is pelletized PVDF monomer produced from the extracted fluorine compound. These early fluorocarbon lines were originally used as leader material only, primarly in saltwater. Sunline was established in 1977 with a focus to create the highest quality line and quickly rose to prominence in the Japanese market. In 1981, Sunline launched Kyokurin Hard which was the first line with a waterproof hard resin coating. Soon after in 1984, Powerd was launched in the Japanese market. Powerd was the first line launched with diameter and knot strength indication listed for the lines. This allowed anglers to know for the first time the actual diameter of the line and comparable tensile strength.
Japanese firm Toyobo and Dutch company DSM succeeded in making high density polyethylene filament in 1988. They created the foundational raw materials used in the production of today’s modern braided lines. Sunline’s first braided line product, Deep One launched in 1992.
Around 1990, bass fisherman began to use fluorocarbon leaders as main line on spinning and baitcast reels. Anglers were looking to capitalize on the characteristics of lower visibility and higher abrasion resistance that they liked in the leaders to use as their main lines full time. Fluorocarbon also provided greater sensitivity for a main line due to it having less stretch than nylon. In 1991, Sunline opened a new factory featuring increased technology and much larger production output per year. In 1992, Sunline started production of Sunline branded fluorocarbon lines, soon after their first braided line product, Deep One launched the same year. These first fluorocarbon lines were tested many times in the lab and on the water with Sunline’s pro angling team. Multiple prototypes were created to insure the final finished product would meet anglers’ needs. Production grew at a rapid pace as the demand for fluorocarbon lines began to build in many markets. In 1993, Sunline launched Tornado their first fluorocarbon leader which began their reputation for high quality fluorocarbon products. In 1999, Sunline launched a new fluorocarbon leader, V Hard that is still very popular and sold today.
The 2000s saw the growth of fluorocarbon expand rapidly with numerous new products launched including FC Sniper, Shooter and FC100 to name a few. Anglers from all markets continued to recognize the benefits of fluorocarbon and the Sunline labatory continued to develop new products for freshwater and saltwater markets. In 2014, Sunline launched it’s first product that had been processed with the P-Ion technology. P-Ion technology was a joint development project with the Tokyo Institue of Technology. The P-Ion process molecularly changes the surface of any line making it more abrasion resistant and slicker allowing for longer casts. The process was in development for over five years in an effort to make the best lines even better with better performance, greater strength and longer casting. The P-Ion process was patented globally and the name was updated to Plasma Rise in 2019.
Line is made using an extrusion system that takes the line through a number of cooling, heating and moisture processes while stretching the line to its final diameter. Controlling the process to the smallest detail is what creates the highest quality lines. The following image shows the extrusion process.
The four biggest reasons anglers continue to prefer fluorocarbon for any species are abrasion resistance, decreased visibility under water, greater sensitivity and no impact from natural conditions like ultraviolet light.
Fluorocarbon has a much greater resistance to abrasion from rocks, trees or fish teeth than nylon lines. Below is a comparison between 10 strokes underwater with 1.3lbs of weight on an abrasion wheel.
While not invisible under water like many people believe, fluorocarbon is less visible under water than nylon. Water has a refractive index of 1.33. Fluorocarbon has a refractive index of 1.42 which is closer to water than the 1.53 of nylon. This is what makes fluorocarbon less visible under water.
Fluorocarbon lines provide greater sensitivity because it is harder and transmits bites better. It also features lower stretch which transmits bites more easily.
Finally, fluorocarbon is not impacted by cold or ultraviolet light like nylon lines. UV light can come from lights in stores or can it can come from sun exposure on your reel when outside. Not being impacted by uv light, allows fluorocarbon lines to maintain their strength longer and allows anglers to use the lines longer without performance suffering.
See below the testing data of both nylon line and flurocrabon that have been exposed to uv light.
Sunline also takes this protection from uv light, one stop further by making sure the top of the spool is covered on all of our filler spool packaging to make sure the spools do not receive any uv light from the top while hanging on the pegs in the stores.
Article courtesy of sunlineamerica.com